Applied Science | Underwater laser cutting and silver sintering to make ceramic circuit boards @AppliedScience | Uploaded 3 years ago | Updated 21 hours ago
Thermal stress cracking can be completely avoided by CO2 laser cutting thin alumina sheets underwater. I also show how to formulate and apply silver paste, then sinter in a kiln to produce double-sided ceramic printed circuit boards with conductive vias.
60W CW CO2 laser at 80% power. 10mm/sec. Standard lens focal length (50mm). 2mm water above ceramic. 180 passes to cut through 0.75mm thick alumina.
Silver paste: 97% silver powder, 3% glass powder by mass. Particle size 1 micron or less. Add poly vinyl alcohol mold release until desired consistency reached.
Paste applied with 4 mil thick vinyl stencil. Dried in air 10 minutes, then rapidly brought up to 900*C, held for 10 minutes, then rapidly brought back down to room temperature. Total cycle about 45 minutes.
I measured electrical conductivity of the finished traces from my process with vinyl stencils: 4 milliohms per square at 10 micron final thickness. This is pretty close to the Dupont published spec ( less than 2 milliohm/sq at 16 micron thick)
Underwater CO2 laser cutting reference: https://sci-hub.se/10.1016/J.JEURCERAMSOC.2011.06.015
60W laser cutter: ebay.com/itm/294386493292
Ceramic sheets at McMaster: mcmaster.com/alumina/nonporous-alumina-ceramic-sheets-and-bars
Ceramic PCB prototypes: ceramic-pcb.com/product/alumina-pcb-al2o3-pcb-prototypes-online
Quickfire kiln: kruegerpottery.com/products/par_quikfire6
Raspberry Pi picoReflow oven controller: apollo.open-resource.org/mission:resources:picoreflow
Silver powder: ebay.com/itm/122525930519
Glass glaze: amazon.com/dp/B0044SCR6O
Macor: mcmaster.com/materials/material~glass-mica-ceramic
Dupont silver paste: dupont.com/content/dam/dupont/amer/us/en/transportation-industrial/public/documents/en/LF131.pdf
Binders for ceramic powder: digitalfire.com/article/binders+for+ceramic+bodies
PVA mold release: tapplastics.com/product/fiberglass/mold_releases/tap_pva_mold_release_liquid/67
Very complete study of laser machining of ceramics: research.manchester.ac.uk/portal/files/54520291/FULL_TEXT.PDF
Applied Science on Patreon: patreon.com/AppliedScience
Thermal stress cracking can be completely avoided by CO2 laser cutting thin alumina sheets underwater. I also show how to formulate and apply silver paste, then sinter in a kiln to produce double-sided ceramic printed circuit boards with conductive vias.
60W CW CO2 laser at 80% power. 10mm/sec. Standard lens focal length (50mm). 2mm water above ceramic. 180 passes to cut through 0.75mm thick alumina.
Silver paste: 97% silver powder, 3% glass powder by mass. Particle size 1 micron or less. Add poly vinyl alcohol mold release until desired consistency reached.
Paste applied with 4 mil thick vinyl stencil. Dried in air 10 minutes, then rapidly brought up to 900*C, held for 10 minutes, then rapidly brought back down to room temperature. Total cycle about 45 minutes.
I measured electrical conductivity of the finished traces from my process with vinyl stencils: 4 milliohms per square at 10 micron final thickness. This is pretty close to the Dupont published spec ( less than 2 milliohm/sq at 16 micron thick)
Underwater CO2 laser cutting reference: https://sci-hub.se/10.1016/J.JEURCERAMSOC.2011.06.015
60W laser cutter: ebay.com/itm/294386493292
Ceramic sheets at McMaster: mcmaster.com/alumina/nonporous-alumina-ceramic-sheets-and-bars
Ceramic PCB prototypes: ceramic-pcb.com/product/alumina-pcb-al2o3-pcb-prototypes-online
Quickfire kiln: kruegerpottery.com/products/par_quikfire6
Raspberry Pi picoReflow oven controller: apollo.open-resource.org/mission:resources:picoreflow
Silver powder: ebay.com/itm/122525930519
Glass glaze: amazon.com/dp/B0044SCR6O
Macor: mcmaster.com/materials/material~glass-mica-ceramic
Dupont silver paste: dupont.com/content/dam/dupont/amer/us/en/transportation-industrial/public/documents/en/LF131.pdf
Binders for ceramic powder: digitalfire.com/article/binders+for+ceramic+bodies
PVA mold release: tapplastics.com/product/fiberglass/mold_releases/tap_pva_mold_release_liquid/67
Very complete study of laser machining of ceramics: research.manchester.ac.uk/portal/files/54520291/FULL_TEXT.PDF
Applied Science on Patreon: patreon.com/AppliedScience